For Sale - RM - 3184
Specification
Reference Number
RM - 3184Location
ChinaProduct Details
- PP Resin
- Melt flow rate (230°C/2.16KG)g/10min 12 g/10min
- Mechnical Properties
- Tensile modulus of elasticity (v=1mm/min): 1550 Mpa
- Tensile yield at stress(v=50mm/min): 35Mpa
- Tensile yield at strain (v=50mm/min): 8%
- Tensile strain at break (v=50mm/min): 50%
- Charpy impact strength unnotched (+23C): 110kJ/m2
- Charpy impact strength notched (+23°C): 3.0kJ/m2
- Izod Impact strength notenched (+23°C): 3kJ/m2
- Ball indentation hardness (H 358/30) 78Mpa
- Melting point, DSC: 163°C
- Heat deflection temperature - HDT/B(0.45Mpa): 85°C
- Vicat softening temperature VST/A50(10N): 154
- Density: 0.91g/cm3
- Melt flow rate (230°C/2.16KG)g/10min 12 g/10min
- Mechnical Properties
- Tensile modulus of elasticity (v=1mm/min): 1550 Mpa
- Tensile yield at stress(v=50mm/min): 35Mpa
- Tensile yield at strain (v=50mm/min): 8%
- Tensile strain at break (v=50mm/min): 50%
- Charpy impact strength unnotched (+23C): 110kJ/m2
- Charpy impact strength notched (+23°C): 3.0kJ/m2
- Izod Impact strength notenched (+23°C): 3kJ/m2
- Ball indentation hardness (H 358/30) 78Mpa
- Melting point, DSC: 163°C
- Heat deflection temperature - HDT/B(0.45Mpa): 85°C
- Vicat softening temperature VST/A50(10N): 154
- Density: 0.91g/cm3