For Sale - RM - 2574
Specification
Reference Number
RM - 2574Location
Far East AsiaProduct Details
PP Homopolymer for Woven Bags:
- Melt flow rate (230 Degree C, 2.16 kg): 3 g/10 min. (Test method: ASTM D1238)
- Density: 0.902 g/cm3 (Test method: ASTM D792)
- Tensile strength at yield: 360 kg/cm2 (Test method: ASTM D638)
- Elongation at yield: 11 percent (Test method: ASTM D638)
- Flexural modulus: 16400 kg/cm2 (Test method: ASTM D790)
- Rockwell hardness: 97 R scale (Test method: ASTM D785)
- Heat deflection temperature: 98 Degree C (Test method: ASTM D648)
- Izod impact strength, notched, 23 Degree C: 3.5 kg-cm/cm (Test method: ASTM D256)
- Mold shrinkage: 1.4 percent (Test method: ASTM D955)
- Quantity: 100 MT
- Packing: 25 kgs / bag, 17 MT/20' or 24 MT/40' without pallet
- Payment: T/T in advance or L/C at sight
- Validity: Feb. 12, 2010
Features:
- High tensile strength
- Good stiffness
- Good stretch ability
- Good mold ability
Typical application:
- Extrusion: thin sheet, band
- Flat yarn: woven bag, jumbo bag
- Injection: closure, appliances.
- Melt flow rate (230 Degree C, 2.16 kg): 3 g/10 min. (Test method: ASTM D1238)
- Density: 0.902 g/cm3 (Test method: ASTM D792)
- Tensile strength at yield: 360 kg/cm2 (Test method: ASTM D638)
- Elongation at yield: 11 percent (Test method: ASTM D638)
- Flexural modulus: 16400 kg/cm2 (Test method: ASTM D790)
- Rockwell hardness: 97 R scale (Test method: ASTM D785)
- Heat deflection temperature: 98 Degree C (Test method: ASTM D648)
- Izod impact strength, notched, 23 Degree C: 3.5 kg-cm/cm (Test method: ASTM D256)
- Mold shrinkage: 1.4 percent (Test method: ASTM D955)
- Quantity: 100 MT
- Packing: 25 kgs / bag, 17 MT/20' or 24 MT/40' without pallet
- Payment: T/T in advance or L/C at sight
- Validity: Feb. 12, 2010
Features:
- High tensile strength
- Good stiffness
- Good stretch ability
- Good mold ability
Typical application:
- Extrusion: thin sheet, band
- Flat yarn: woven bag, jumbo bag
- Injection: closure, appliances.
{{comment.DateTimeStampDisplay}}
{{comment.Comments}}