| Description of Material :- Nylon-6 Unfilled Black Compound | |||
| Application :- Textile , Automotive ,Appliances, Electricals | |||
PROPERTIES |
ASTM TEST METHOD |
UNITS |
VALUE |
PHYSICAL |
|||
Density |
D-1505 |
Gm/cm3 |
1.12 ± 0.05 |
Melt Flow Index @2.16 Kgf Load |
D-1238 |
Gm/ 10 min. |
NA |
Moisture Absorption |
D-570 |
% |
0.10 ~ 0.50 |
Mould Shrinkage |
-- |
% |
1.40± 0.05 |
Melting Point |
D-2117 |
0C |
-- |
MECHANICAL |
|||
Tensile Strength at Yield |
D-638 |
Kg/cm2 |
590 |
Elongation at Break |
D-638 |
% |
55 |
Flexural Strength |
D-790 |
Kg/cm2 |
950 |
Flexural Modulus |
D-790 |
Kg/cm2 |
23500 |
Izod Impact - Notched at 230C |
D-256 |
Kg-cm/cm |
5.50 |
Rockwell Hardness |
D-785 |
R-scale |
-- |
THERMAL |
|||
HDT at 4.6 Kgf Load |
D-648 |
0C |
142 |
Flammability at 1.6mm thickness |
UL-94 |
Rating |
NA |
PROCESSING GUIDELINES |
|||
Pre Drying Temperature |
-- |
0C |
90 0C |
Pre Drying Time |
-- |
Hour |
3 |
Melt Temperature |
|||
Feed |
-- |
0C |
250 |
Compression |
-- |
0C |
260 |
Metering |
-- |
0C |
270 |
Nozzle |
-- |
0C |
260 |
Mould Temperature |
-- |
0C |
60 ~ 90 |
Injection Pressure |
-- |
-- |
900 ~ 1400 |
Injection Speed |
-- |
-- |
Medium |
Back Pressure |
-- |
Bar |
LOW |
Screw Speed |
-- |
RPM |
LOW |