Manufacture, Distribution, Import and Export of Polymers and Additives

Intercontinental Polymer Private Limited (IPPL) is an indo-American joint venture involved in the manufacture, distribution, import and export of a wide range of Polymers and Additives. IPPL offers customized, product-specific compounds and provides the highest value proposition to its customers. As a group, the company delivers total solutions – right from product design & development to mold flow analysis, tool design, fabrication and molding.
Located in Daman, India’s cost-effective Union Territory, IPPL has been operating under the aegis of a highly professional team of chemical and plastics engineers who have a combined experience of over 45 years in the field. After exploring the rising potential of engineering thermoplastic compounds in India and the world, IPPL has enhanced its capacity by installing the most technically- advanced manufacturing lines. The facility incorporates a fully computerized quality system for monitoring and maintaining consistency at every stage and is backed by a ultramodern testing laboratory. IPPL has associate manufacturing units In USA, Canada, Mexico and China. This helps the company in meeting requirements of engineering thermoplastic compounds in any corner of the world- at competitive prices. For applications in IT, Automobiles, Electrical, Electronics, white Goods and Telecommunication, IPPL also offers complete technical support.
Manufacturing Facilities
Computerised Twin Screw Extruder, Universal Testing Machine, Analogue Izod / Charpy Impact Tester, Melt Flow Index Tester

Engineering Plastic Compounds

Polyamide (Nylon) 66 – 33% Glass Filled - IPLON

Product: NYLON 66 - 33% Glass Filled
Grade: N6633GFBK
Colour: Black
PROPERTY  TEST METHOD  UNIT  VALUE
Specific Gravity ASTM D 792 -----  1.39
Heat Deflection Temp ASTM D 648 at 18.5 Kg/cm²  220°C
Tensile Strength at yield ASTM D 638 MPa  170
Elongation at break ASTM D 638 %  6
Flexural Strength ASTM D 790 MPa  190
Modulus of Elasticity  (Flexural) ASTM D 790 MPa  6500
IZOD Impact Strength ASTM D 256 kg cm/cm of Notch  8/20 *
* Conditioned Test Specimen
Note: The Values stated above are indicative only, based on our knowledge and experience. These do not constitute a warranty
Processing Conditions
• Pre-Drying Temperature / Time: 80° – 100° C / 2 - 4 Hours
• Recommended Melt Temperature: 200° – 325° C (Nozzle)
• Recommended Mold Temperature: 80° C
• Injection Pressure: High; Low Back Pressure
• Injection Speed: Medium to High
Applications: Automotive Parts, Electrical & Electronic Components, Bobbins, Switch Gears, Furniture & Fixtures, Housings of Hand Tools

Polyamide (Nylon) 6 - 30% Glass Filled - IPLON

Product: NYLON 6 - 33% Glass Filled
Grade: N630GFBK
Colour: Black
PROPERTY  TEST METHOD  UNIT  VALUE
Specific Gravity ASTM D 792 -----  1.36
Heat Deflection Temp ASTM D 648 at 18.5 kg/cm²  220°C
Tensile Strength at yield ASTM D 638 MPa  165
Elongation at break ASTM D 638 %  7
Flexural Strength ASTM D 790 MPa  180
Modulus of Elasticity(Flexural) ASTM D 790 MPa  6000
IZOD Impact Strength ASTM D 256 kg cm/cm of Notch  10/22 *
* Conditioned Test Specimen
Note: The Values stated above are indicative only, based on our knowledge and experience. These do not constitute a warranty
Processing Conditions
• Pre-Drying Temperature / Time: 80° – 100° C / 2 - 4 Hours
• Recommended Melt Temperature: 200° – 325° C (Nozzle)
• Recommended Mold Temperature: 80° C
• Injection Pressure: High; Low Back Pressure
• Injection Speed: Medium to High
Applications: Automotive Parts, Electrical & Electronic Components, Bobbins, Switch Gears, Furniture & Fixtures, Housings of Hand Tools

PPO – Glass Fiber Reinforced - IPTHER

Product: PPO – 30% Glass Filled
Grade: PPO30GFBK
Colour: Black
PROPERTY TEST METHOD   UNIT VALUE
Specific Gravity ASTM D 792 ----- 1.30
Heat Deflection Temp ASTM D 648 @18.5 Kg/cm² 140°C
Tensile Strength at yield ASTM D 638 MPa 100
Elongation at break ASTM D 638 % 1.5
Flexural Strength ASTM D 790 MPa 125
Modulus of Elasticity  (Flexural) ASTM D 790 MPa 6000
IZOD Impact Strength ASTM D 256 kg cm/cm of Notch 25 *
* Un-Notched
Note: The Values stated above are indicative only, based on our knowledge and experience. These do not constitute a warranty
Processing Conditions
• Pre- Drying Temperature / Time: 100° - 120° C / 2- 4 Hours
• Recommended Melt Temperature: 280° – 300° (Nozzle)
• Recommended Mold Temperature: 80° – 120° C
• Injection Pressure: Medium; Low Back Pressure
• Injection Speed: Medium
Applications: Meter Housings, Appliance Housings, Underwater Applications such as Pump Parts

PBT – Antistatic/Glass Reinforced - IPLITE

Product: PBT– 30% Glass Filled
Grade: PBT30GFN
Colour: Natural
PROPERTY TEST METHOD   UNIT VALUE
Specific Gravity ASTM D 792 ----- 1.53
Heat Deflection Temp ASTM D 648 at18.5 Kg/cm² 205°C
Tensile Strength at yield ASTM D 638 MPa 125
Elongation at break ASTM D 638 % 3
Flexural Strength ASTM D 790 MPa 195
Modulus of Elasticity  (Flexural) ASTM D 790 MPa 7500
IZOD Impact Strength ASTM D 256 kg cm/cm of Notch 8
Note: The Values stated above are indicative only, based on our knowledge and experience. These do not constitute a warranty
Processing Conditions
• Pre-Drying Temperature / Time: 80° – 100° C / 2 – 4 Hours
• Recommended Melt Temperature: 200° – 275° (Nozzle)
• Recommended Mold Temperature: 80° C
• Injection Pressure: Medium; Low Back Pressure
• Injection Speed : Medium
Applications: Electrical Insulation, MCB / ELCH Components, Coil Formers, Bobbins, Housings For Lighting & Appliances, Pump Housings, Textile Components

PP – Glass Fiber Reinforced - IPYLENE

Product: PP - 20% Talc Filled
Grade: PP20TBK
Colour: Black
PROPERTY TEST METHOD   UNIT VALUE
 Specific Gravity ASTM D 792 ----- 1.04
 Heat Deflection Temp ASTM D 648 at 18.5 Kg/cm² 70° C
 Tensile Strength at yield ASTM D 638 MPa 32
 Elongation at break ASTM D 638 % 12
 Flexural Strength ASTM D 790 MPa 40
 Modulus of Elasticity  (Flexural) ASTM D 790 MPa 2440
 IZOD Impact Strength ASTM D 256 kg cm/cm of Notch 4.5*
* Conditioned Test Specimen
Note: The Values stated above are indicative only, based on our knowledge and experience. These do not constitute a warranty
Processing Conditions
• Pre- Drying Temperature / Time: 50° C / 2hours
• Recommended Melt Temperature: 200° – 250° (Nozzle)
• Recommended Mold Temperature: 40° – 45° C
• Injection Pressure: Medium; Low Back Pressure
• Injection Speed: Medium
Applications: Automobile Components, Furniture, Pump Housings Washing Machine Components Defense Applications

Other Products

• Acrylics
• Thermoplastic Polyester Elastomer
• CA, CAB, CAP
• Hydrocarbon Resin
• PVC Impact Modifier
• PET - Glass filled
• Sulpho Polymer


Polyamide (Nylon) 66 - IPLON | Polyamide (Nylon) 6 - IPLON | PPO - IPTHER | PBT - IPLITE | PP - IPYLENE

Top
Contact Us
Company Name
Intercontinental Polymer Private Limited (IPPL)
Contact Person Mr. Sanjay Master
Address 101, Advent Atria, Chincholi Bunder Road, Malad (West), Mumbai 400064, Maharashtra, India
Contact Number
+91 22 28886767 / 68
Contact Number
+91 22 28820629
Email info@ipplmail.com, master@ipplmail.com, niharika@ipplmail.com
Website
www.intercontinentalpolymers.com
Enquiry
Close Window