PEEK Can Be 3D Printed To Make Durable, Lightweight And Geometrically Complex Carbon Fiber Composite Parts.

PEEK can be 3D printed to make durable, lightweight and geometrically complex carbon fiber composite parts.

16-Jul-16

Illinois-based 3D printing materials sciences company Impossible Objects announced that they have developed a method of using PEEK (polyetheretherketone) with their revolutionary Composite-Based Additive Manufacturing (CBAM) process. For the first time the high-performance thermoplastic PEEK can be 3D printed to make durable, lightweight and geometrically complex carbon fiber composite parts. Because PEEK offers exceptional strength along with superior heat and chemical resistance, Impossible Objects is now capable of producing parts for applications that previously were virtually impossible. Industries as diverse as aerospace, medical, automotive and machine tooling will have access to a material that offers properties typically only found in metals.

Parts that are produced using PEEK with the CBAM process have been thoroughly tested and ended up performing extremely well. CBAM PEEK parts will perform more than 30% better than CBAM parts using traditional materials. The parts also have a tensile strength of 205 MPa (29,700 psi) with an impressive heat resistance of 250°C (482°F). Combined with the freedom of virtually unlimited geometry and fast production times that are offered with the CBAM process, carbon fiber-PEEK composite parts can be used in the place of many heavier and more limited metal parts.
The CBAM process developed by Impossible Objects is the first truly new 3D printing technology that has been developed in more than 20 years. CBAM uses conventional thermal inkjet heads to print individual layers on sheets of composite materials, including carbon fiber, Kevlar or fiberglass. The sheet is then coated with powdered polymers like nylon or PEEK, which sticks to the still-wet pattern printed in inkjet fluids. Just as with a 2D printer or copier, each layer of the 3D object is printed off individually. Once the excess powder materials are vacuumed off, the sheets are stacked in order before being compressed and heated until the powder melts, which binds the patterns together to form a fully-solid part.

Once all of the layers have been successfully bonded together, the remainder of the sheets of carbon fiber are removed, either with sandblasting or chemical treatments. The remaining part offers strong and lightweight properties that are impossible to manufacture as quickly and inexpensively. Because the final parts match the strength-to-weight ratio of many common industrial-use metals, the process is ideal for applications that have critical weight and durability requirements as well as a need for air- and water-tight features. Industries like aerospace, aviation, automotive, defense, oilfield services and performance athletics will especially benefit from this new 3D printing process and advanced materials. You can see video of the process here. CBAM parts made with PEEK are up to 10 times stronger and can be manufactured up to 100 times faster than traditional methods. Standard CBAM parts made with carbon fiber or nylon have a tensile strength of 150 MPa (21,700 psi) with a heat resistance of 120°C (248°F). Alternately, CBAM parts made with PEEK perform more than 30% better, have a tensile strength of 205 MPa (29,700 psi) with a heat resistance of 250°C (482°F). They are also more than 50% lighter than traditional aluminum parts while maintaining 2/3rds of the strength. The PEEK composite materials are also recyclable.