IIT (BHU) Detailed Study Shows Waste Plastics Road Retains Mechanical Properties

IIT (BHU) Detailed Study Shows Waste Plastics Road Retains Mechanical Properties

IIT (BHU) Detailed Study Shows Waste Plastics Road Retains Mechanical Properties
Ujjwal Srivastava, Shivaji Hemant Wankhade, Dipti Saxena and Pralay Maiti School of Materials Science and Technology,
Indian Institute of Technology (BHU),Varanasi, 221005

Despite certain steps undertaken for controlling land pollution, there isn't much changes in the environmental condition caused by the polyethylene wastes (Fig. 1). Global production of plastics is about 310 metric tons per year that need to be consumed to prevent further environmental losses.
About 1.15 km length of road covers 9000m2 of area, which requires about 600 tons of bitumen. Adding 50% polyethylene would allow us to give space for 300 tons of polyethylene. Shredded waste plastics may be used along with bitumen for road construction (Fig. 2).

Fig.1: Plastic wastes in the bank of river Ganges

Fig.2: Shredded plastic taken from the waste in the river Ganges
2.Idea behind our work
The idea behind our project is to use optimized mixture ratio of polyethylene and bitumen with gravel in the construction of road instead of conventional mixture of bitumen with gravel (control).
Generally, about 10% of Bitumen is mixed with 90% gravel (by weight) for normal road construction. Our idea focused on using about 50-50 mixture ratio of polyethylene and bitumen and further using it with 90% gravels in the construction of road to reduce the effect of so called plastic pollution.
The toughness of plastic filled gravel is more that only bitumen filled gravel though the elastic modulus slightly reduce in plastic filled gravel (Table 1). Thus, our work demonstrate the use of waste plastic for road construction by reducing the plastic pollution at lower road repairing cost without the bad effect (as evident from no distortion of repaired busy road even after six months).
Bitumen with gravel Polyethylene + Bitumen with gravel
Toughness: 4.3 kJ/m3
Modulus: 30.0 MPa
Elongation at break: 18.36 %
Tensile strength: 0.06 MPa
Toughness: 4.8 kJ/m3
Modulus: 21.3 MPa
Elongation at break: 30.54 %
Tensile strength: 0.05 MPa
Table 1: Comparison of mechanical strength of plastic filled gravel with conventional bitumen filled gravel (control).

Thus, our developed material demonstrate the efficacy of road repairing material where 50% waste plastic can be used which will reduce the plastic pollution along with lower cost of road repairing. This idea may be extended to road construction as well using waste plastic at large scale.
3. Repairing of road using waste polyethylene
Figure 3 shows images of the 'pothole' and 'filled pothole' by using mixture of polyethylene and bitumen with gravel at different time interval up to six months which clearly demonstrate that no pothole generated over the repaired pothole or in other words there is no damages on the repaired potholes and act like repaired with conventional bitumen treated road repairing. To understand the strength of plastic mixed bitumen against pure bitumen, tensile tests were performed with gravel mixture. Figure 4 shows the stress-strain curves of plastic filled construction materials vis-a-vis only bitumen filled gravel (control).

Fig.3 : Images of road condition of pothole before and after
repairing with the developed material

Fig.4 : Stress-strain curve of 'Bitumen with Gravel' and 'Polyethylene + Bitumen with Gravel'.
  Back to Articles
{{comment.Name}} made a post.




There are no comments to display. Be the first one to comment!


Name Required.


Email Id Required.

Email Id Not Valid.


Mobile Required.

Email ID and Mobile Number are kept private and will not be shown publicly.

Message Required.

Click to Change image  Refresh Captcha



Moulds for lotion pump

Moulds for lotion pump